A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
DescriptionPolyfort® FPP 3711 is a 26% calcium carbonate filled high impact polypropylene.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 177 % | 177 % | ASTM D638 |
| Flexural Strength | 32.0 MPa | 4640 psi | ASTM D790 |
| Flexural Modulus | 1.511 GPa | 219.2 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ASTM D648 |
| Flammability, UL94 | HB
@Thickness 1.57 mm
|
HB
@Thickness 0.0618 in
|
|
| HB
@Thickness 3.05 mm
|
HB
@Thickness 0.120 in
|