A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
| Manufacturer | A. Schulman, Inc. |
| Trade Name | POLYFORT™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 54.0 MPa | 7830 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |