Aclo Accutech Polypropylene Homopolymer HP0334W10L1 Wollastonite Reinforced
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | MD; ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89 | 89 | ASTM D785 |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM D638 |
| Elongation at Break | 28 % | 28 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Izod Impact, Notched | 0.539 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F |