Arkema Group Oroglas® DRT Acrylic, Impact Grade (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
For extrusion and injection molding applications. OROGLAS DRT combines good thermal resistance with an excellent impact resistance.Key features : impact resistance: up to 10 times more impact-resistant than standard acrylic high temperature resistance: HDT A / 1.82 MPa = 88°c clarity and low haze UV stability easy processing Typical applications: indoor and outdoor lighting applications appliances and house ware items automotive signs OROGLAS DRT is also used as top layer, alone or in coextrusion for sanitary, garden furniture, pools, window profiles and automotive fields.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Water Absorption | 2.0 % | 2.0 % | |
| Moisture Absorption at Equilibrium | 0.36 % | 0.36 % | Humidity Absorption |
| Melt Flow | 0.80 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
0.80 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min |
| Elongation at Break | 40 % | 40 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C
@Temperature 20.0 °C
|
55.6 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | |
| Vicat Softening Point | 93.0 °C | 199 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Mfr. reports ‘Transparent’ but doesn’t quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.2
@Frequency 1e+6 Hz
|
3.2
@Frequency 1e+6 Hz
|
|
| 3.9
@Frequency 100 Hz
|
3.9
@Frequency 100 Hz
|
||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | |
| Dissipation Factor | 0.040
@Frequency 1e+6 Hz
|
0.040
@Frequency 1e+6 Hz
|
|
| 0.050
@Frequency 100 Hz
|
0.050
@Frequency 100 Hz
|
||
| Comparative Tracking Index | 600 V | 600 V |