Arkema Group Oroglas® HFI-10 Acrylic, Impact Grade (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
OROGLAS HFI-10 is an impact grade that in addition to its superior impact resistance provides an improvement in flow which contribute to improve molding behavior and reduce cycle time.Key features : impact resistance: up to 10 times more impact-resistant than standard acrylic easy processing: flow significantly improved which contribute to reduce cycle time by 20 %. ( MFI, 230°c/3.8 kg ) = 3 gr / 10 min ( MVI, 230°c/3.8 kg ) = 2.8 ml / 10 min excellent optical properties with low edge color UV stability Typical applications : OROGLAS HFI-10 can be injection molded or extruded in any type of machine Typical applications are in the fields of: building, lighting, appliances, information technology, and business machines. OROGLAS HFI-10 is recommended when toughness and increased flow are required.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Water Absorption | 2.0 % | 2.0 % | |
| Moisture Absorption at Equilibrium | 0.36 % | 0.36 % | Humidity Absorption |
| Melt Flow | 2.8 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
2.8 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min |
| Elongation at Break | 30 % | 30 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 1400 MPa | 203000 psi | |
| Tensile Creep Modulus, 1000 hours | 1000 MPa | 145000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C
@Temperature 20.0 °C
|
55.6 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | |
| Vicat Softening Point | 84.0 °C | 183 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Mfr. reports ‘Transparent’ but doesn’t quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.2
@Frequency 1e+6 Hz
|
3.2
@Frequency 1e+6 Hz
|
|
| 3.9
@Frequency 100 Hz
|
3.9
@Frequency 100 Hz
|
||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | |
| Dissipation Factor | 0.040
@Frequency 1e+6 Hz
|
0.040
@Frequency 1e+6 Hz
|
|
| 0.050
@Frequency 100 Hz
|
0.050
@Frequency 100 Hz
|
||
| Comparative Tracking Index | 600 V | 600 V |