BASF Ultrason® KR 4113 PESU with 10/10% Carbon Fibers/Graphite and 10% PTFE
| Manufacturer | BASF |
| Trade Name | Ultrason® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibers, graphite and PTFE powder, considerably improves Ultrason’s tribological properties. In addition, this product has a very small expansion coefficient and low tendency to swell in hot oils. Abbreviated designation according to ISO 1043-1: PESU-(CF+ZD)Typical applications: Oil control piston in standard automotive oil pumps and oil control piston in volume controlled automotive oil-pumpsInformation provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 – 0.800 g/cc | 0.0253 – 0.0289 lb/in³ | |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 % | 1.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.50 % | 0.50 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 56 | 56 | [cm<sup>3</sup>/g]; ISO 307 |
| Linear Mold Shrinkage, Flow | 0.0031 cm/cm | 0.0031 in/in | ISO 2577, 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0046 cm/cm | 0.0046 in/in | ISO 2577, 294-4 |
| Melt Flow | 14.8 g/10 min
@Load 10.0 kg,
Temperature 360 °C |
14.8 g/10 min
@Load 22.0 lb,
Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 180 MPa
@Load 98.0 kg,
Time 30.0 sec |
26100 psi
@Load 216 lb,
Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength | 108 MPa
@Treatment Temp. 150 °C,
Time 7.20e+6 sec |
15700 psi
@Treatment Temp. 302 °F,
Time 2000 hour |
used oil |
| 108 MPa
@Treatment Temp. 150 °C,
Time 1.08e+7 sec |
15700 psi
@Treatment Temp. 302 °F,
Time 3000 hour |
used oil | |
| 109 MPa
@Treatment Temp. 150 °C,
Time 7.20e+6 sec |
15800 psi
@Treatment Temp. 302 °F,
Time 2000 hour |
new oil | |
| 109 MPa
@Treatment Temp. 150 °C,
Time 3.60e+6 sec |
15800 psi
@Treatment Temp. 302 °F,
Time 1000 hour |
used oil | |
| 110 MPa
@Treatment Temp. 150 °C,
Time 3.60e+6 sec |
16000 psi
@Treatment Temp. 302 °F,
Time 1000 hour |
new oil | |
| 111.0 MPa
@Treatment Temp. 150 °C,
Time 1.08e+7 sec |
16100 psi
@Treatment Temp. 302 °F,
Time 3000 hour |
new oil | |
| 112 MPa
@Treatment Temp. 150 °C,
Time 0.000 sec |
16200 psi
@Treatment Temp. 302 °F,
Time 0.000 hour |
new oil | |
| 112 MPa
@Treatment Temp. 150 °C,
Time 0.000 sec |
16200 psi
@Treatment Temp. 302 °F,
Time 0.000 hour |
used oil | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 50mm/min; ISO 527-1/-2 |
| Elongation at Yield | 1.3 % | 1.3 % | 50mm/min; ISO 527-1/-2 |
| Tensile Modulus | 10.1 GPa | 1460 ksi | ISO 527-1/-2 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m²
@Temperature 23.0 °C
|
2.38 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/A |
| Charpy Impact Unnotched | 1.90 J/cm²
@Temperature 23.0 °C
|
9.04 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm²
@Temperature -30.0 °C
|
1.43 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| 0.450 J/cm²
@Temperature 23.0 °C
|
2.14 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
6.11 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 75-1/-2 |
| 13.0 µm/m-°C
@Temperature 180 °C
|
7.22 µin/in-°F
@Temperature 356 °F
|
DIN 53752 | |
| 26.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 25.0 °C |
14.4 µin/in-°F
@Thickness 0.157 in,
Temperature 77.0 °F |
||
| 26.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 75.0 °C |
14.4 µin/in-°F
@Thickness 0.157 in,
Temperature 167 °F |
||
| 27.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 125 °C |
15.0 µin/in-°F
@Thickness 0.157 in,
Temperature 257 °F |
||
| 27.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 175 °C |
15.0 µin/in-°F
@Thickness 0.157 in,
Temperature 347 °F |
||
| 33.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 25.0 °C |
18.3 µin/in-°F
@Thickness 0.0787 in,
Temperature 77.0 °F |
||
| 33.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 75.0 °C |
18.3 µin/in-°F
@Thickness 0.0787 in,
Temperature 167 °F |
||
| 34.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 125 °C |
18.9 µin/in-°F
@Thickness 0.0787 in,
Temperature 257 °F |
||
| CTE, linear, Transverse to Flow | 19.5 µm/m-°C
@Thickness 2.00 mm,
Temperature 125 °C |
10.8 µin/in-°F
@Thickness 0.0787 in,
Temperature 257 °F |
|
| 20.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 75.0 °C |
11.1 µin/in-°F
@Thickness 0.0787 in,
Temperature 167 °F |
||
| 20.0 µm/m-°C
@Thickness 2.00 mm,
Temperature 25.0 °C |
11.1 µin/in-°F
@Thickness 0.0787 in,
Temperature 77.0 °F |
||
| 23.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 75.0 °C |
12.8 µin/in-°F
@Thickness 0.157 in,
Temperature 167 °F |
||
| 24.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 125 °C |
13.3 µin/in-°F
@Thickness 0.157 in,
Temperature 257 °F |
||
| 24.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 25.0 °C |
13.3 µin/in-°F
@Thickness 0.157 in,
Temperature 77.0 °F |
||
| 25.0 µm/m-°C
@Thickness 4.00 mm,
Temperature 175 °C |
13.9 µin/in-°F
@Thickness 0.157 in,
Temperature 347 °F |
||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ISO 11357-1/-2 |
| Decomposition Temperature | >= 400 °C | >= 752 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8500 ohm-cm | 8500 ohm-cm | IEC 60093 |
| Surface Resistance | 4000 ohm | 4000 ohm | IEC 60093 |
| Dielectric Strength | 8.00 kV/mm | 203 kV/in | DIN 53752 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper throat |
| Zone 1 | 350 °C | 662 °F | Feed zone |
| Zone 2 | 360 °C | 680 °F | Compression |
| Zone 3 | 370 °C | 698 °F | Metering-zone |
| Zone 4 | 370 °C | 698 °F | Nozzle |
| Melt Temperature | 350 – 390 °C | 662 – 734 °F | Injection molding/extrusion |
| 370 °C | 698 °F | Optimal | |
| Mold Temperature | 150 – 190 °C | 302 – 374 °F | Injection molding |
| 170 °C | 338 °F | Optimal | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | Europe | |
| Ignition Temperature | >500°C | ASTM D1929 |
| Primary Processing Technique | Injection molding and Extrusion |