Bhansali Engineering Santron IMS1000 Sparkle SAN Resin
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
High Transparent SANInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00400 – 0.00500 cm/cm | 0.00400 – 0.00500 in/in | ASTM D955 |
| Melt Flow | 35.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
35.0 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 63.7 MPa
@Thickness 3.20 mm
|
9250 psi
@Thickness 0.126 in
|
Type I, 5 mm/min; ASTM D638 |
| 68.6 MPa
@Thickness 3.20 mm
|
9960 psi
@Thickness 0.126 in
|
Type I, 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 98.1 MPa
@Thickness 6.40 mm
|
14200 psi
@Thickness 0.252 in
|
5 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm
@Thickness 3.20 mm
|
0.551 ft-lb/in
@Thickness 0.126 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C
@Thickness 6.40 mm
|
203 °F
@Thickness 0.252 in
|
Method A; ASTM D648 |
| Flammability, UL94 | HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |