Description
Material Notes:
Daplen ED206HP is a 25% mineral reinforced compound intended for injection molding. ED206HP has been developed especially for the car industry, to be used in interior parts requiring excellent scratch resistance. ED206HP has good processability with optimized physical properties.Daplen ED205HP has been developed especially for dashboards, interior panels, dashboard inserts, door panels and pockets, and consoles.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Borealis Method |
| Melt Flow | 7.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
7.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 30 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
30 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 50 | 50 | ISO 868 |
| Ball Indentation Hardness | 35.0 MPa | 5080 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | At 50 mm/min; ISO 527-2 |
| Flexural Strength | 20.0 MPa | 2900 psi | ISO 178 |
| Flexural Modulus | 1.92 GPa | 278 ksi | At 2 mm/min; ISO 527-2 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 6.20 J/cm²
@Temperature -20.0 °C
|
29.5 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eA |
| 0.400 J/cm²
@Temperature -30.0 °C
|
1.90 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA | |
| 0.520 J/cm²
@Temperature -20.0 °C
|
2.47 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-2 |
| Vicat Softening Point | 56.0 °C | 133 °F | B (50N); ISO 306 |
| 135 °C | 275 °F | A (10N); ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | |
| Mold Temperature | 30.0 – 60.0 °C | 86.0 – 140 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Emissions, ug C/g | 24 | VDA 277 |
| Fogging % | 98 | At 100°C/3 hours |
| Fogging, mg | 0.4 | At 100°C/ 16 hours |