Borealis Daplen™ EE065AI Polypropylene Elastomer Modified
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen™ EE065AI is an elastomer modified polypropylene with increased crystallinity. This material has an excellent balance between impact strength and stiffness. The product is available in natural color. Applications: automotive interior parts including door panels and pockets, and center consoles.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | Borealis Method |
| Melt Flow | 11.5 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
11.5 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 43.0 MPa | 6240 psi | H 358/30; ISO 2039 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-2 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 150 % | 150 % | 50mm/min; ISO 527-2 |
| Elongation at Yield | 5.1 % | 5.1 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 22.5 MPa | 3260 psi | 3.5% strain; ISO 178 |
| 25.0 MPa | 3630 psi | ISO 178 | |
| Flexural Modulus | 1.00 GPa | 145 ksi | 2mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m²
@Temperature -20.0 °C
|
4.04 ft-lb/in²
@Temperature -4.00 °F
|
ISO 180/1A |
| 50.0 kJ/m²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 200 kJ/m²
@Temperature -20.0 °C
|
95.2 ft-lb/in²
@Temperature -4.00 °F
|
ISO 180/1U |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 180/1U | |
| Charpy Impact Unnotched | 22.0 J/cm²
@Temperature -20.0 °C
|
105 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm²
@Temperature -20.0 °C
|
4.28 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 5.50 J/cm²
@Temperature 23.0 °C
|
26.2 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 |
| Vicat Softening Point | 56.0 °C
@Load 5.10 kg
|
133 °F
@Load 11.2 lb
|
ISO 306 |
| 143 °C
@Load 1.02 kg
|
289 °F
@Load 2.25 lb
|
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 – 260 °C | 428 – 500 °F | mass temperature |
| Feed Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F | |
| Injection Velocity | 100 – 200 mm/sec | 3.94 – 7.87 in/sec | |
| Hold Pressure | 3.00 – 6.00 MPa | 435 – 870 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Emission (µgC/g) | < 50 | VDA 227 |
| Fogging (mg) | <2 | DIN 75201 |
| Screw Speed | low to medium |