Borealis Daplen™ EE103AE TPO Compound
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen EE103AE is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE103AE is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EE103AE has been developed especially for bumpers and exterior trims.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Borealis Method |
| Melt Flow | 12 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
12 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 60 % | 60 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 5.0 % | 5.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.40 GPa | 203 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Strength | 24.5 MPa | 3550 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | At 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB
@Temperature -20.0 °C
|
NB
@Temperature -4.00 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 67.0 µm/m-°C
@Temperature -30.0 – 80.0 °C
|
37.2 µin/in-°F
@Temperature -22.0 – 176 °F
|
Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-2 |
| Vicat Softening Point | 45.0 °C | 113 °F | B (50N); ISO 306 |
| Shrinkage | 0.150 %
@Temperature 90.0 °C,
Time 7200 sec |
0.150 %
@Temperature 194 °F,
Time 2.00 hour |
Post Shrinkage; Borealis Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F |