Borealis Daplen™ EE115T TPO Compound
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen EE115T is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE115T is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EE115T has been developed especially for bumpers, spoilers and exterior trims.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0085 – 0.0095 cm/cm | 0.0085 – 0.0095 in/in | Borealis Method |
| Melt Flow | 10 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
10 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 35.0 MPa | 5080 psi | At 132 N/10 sec; ISO 2039 |
| Tensile Strength, Yield | 17.00 MPa | 2465 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 450 % | 450 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.15 GPa | 167 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.10 GPa | 160 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB
@Temperature -20.0 °C
|
NB
@Temperature -4.00 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm²
@Temperature -30.0 °C
|
2.38 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA | |
| 0.650 J/cm²
@Temperature -20.0 °C
|
3.09 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | <= 85.0 µm/m-°C
@Temperature -30.0 – 80.0 °C
|
<= 47.2 µin/in-°F
@Temperature -22.0 – 176 °F
|
Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ISO 75-2 |
| Vicat Softening Point | 126 °C | 259 °F | A (10N); ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F |