Borealis Daplen™ EE158AI Polypropylene TPO Compound
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen™ EE158AI is a 13% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process. Applications: Daplen™ EE158AI has been developed especially for the car industry to be used in automotive interior parts including dashboards, pillar trims, door panels and pockets, trunk claddings and other automotive interior partsInformation provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.980 g/cc | 0.0354 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.00090 cm/cm | 0.00090 in/in | Borealis Method; anisotropic shrinkage |
| 0.0090 cm/cm | 0.0090 in/in | Borealis Method; isotropic shrinkage | |
| Melt Flow | 11 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
11 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.75 GPa | 254 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm²
@Temperature -20.0 °C
|
28.6 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU |
| 17.0 J/cm²
@Temperature 23.0 °C
|
80.9 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm²
@Temperature -20.0 °C
|
2.38 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 2.50 J/cm²
@Temperature 23.0 °C
|
11.9 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ISO 75-2 |
| Vicat Softening Point | 55.0 °C
@Load 5.10 kg
|
131 °F
@Load 11.2 lb
|
ISO 306 |
| 131 °C
@Load 1.02 kg
|
268 °F
@Load 2.25 lb
|
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 – 260 °C | 428 – 500 °F | mass temperature |
| Feed Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F | |
| Injection Velocity | 100 – 200 mm/sec | 3.94 – 7.87 in/sec | |
| Hold Pressure | 30.0 – 60.0 MPa | 4350 – 8700 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Emission (µgC/g) | 50 | VDA 277 |
| Fogging (mg) | < 2 | DIN 75201;100°C, 16h |
| Screw Speed | low to medium |