Borealis Daplen™ EE189AI Polypropylene TPO Compound
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Material Notes:
Daplen™ EE189AI is a 15% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications: Daplen™ EE189AI has been developed especially for the car industry to be used in automotive interior parts including dashboards, door panels and pockets, and other automotive interior partsInformation provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | mold average;Borealis Method |
| Melt Flow | 11 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
11 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 40 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
40 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | 358 N/30s; ISO 2039 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 21 % | 21 % | 50mm/min; ISO 527-2 |
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 6.50 J/cm²
@Temperature -20.0 °C
|
30.9 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.450 J/cm²
@Temperature -20.0 °C
|
2.14 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 1.60 J/cm²
@Temperature 23.0 °C
|
7.61 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 |
| Vicat Softening Point | 55.0 °C
@Load 5.10 kg
|
131 °F
@Load 11.2 lb
|
ISO 306 |
| 136 °C
@Load 1.02 kg
|
277 °F
@Load 2.25 lb
|
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 – 260 °C | 428 – 500 °F | mass temperature |
| Feed Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F | |
| Injection Velocity | 100 – 200 mm/sec | 3.94 – 7.87 in/sec | |
| Hold Pressure | 3.00 – 6.00 MPa | 435 – 870 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Emission (µgC/g) | < 50 | VDA 277 |
| Fogging (mg) | < 2 | DIN 75201;100°C, 16h |
| Screw Speed | low to medium |
Description
Material Notes:
Daplen™ EE189AI is a 15% mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications: Daplen™ EE189AI has been developed especially for the car industry to be used in automotive interior parts including dashboards, door panels and pockets, and other automotive interior partsInformation provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | mold average;Borealis Method |
| Melt Flow | 11 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
11 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 40 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
40 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 50.0 MPa | 7250 psi | 358 N/30s; ISO 2039 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50mm/min; ISO 527-2 |
| Elongation at Break | 21 % | 21 % | 50mm/min; ISO 527-2 |
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.85 GPa | 268 ksi | 1mm/min; ISO 527-2 |
| Flexural Strength | 30.0 MPa | 4350 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 6.50 J/cm²
@Temperature -20.0 °C
|
30.9 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.450 J/cm²
@Temperature -20.0 °C
|
2.14 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 1.60 J/cm²
@Temperature 23.0 °C
|
7.61 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 |
| Vicat Softening Point | 55.0 °C
@Load 5.10 kg
|
131 °F
@Load 11.2 lb
|
ISO 306 |
| 136 °C
@Load 1.02 kg
|
277 °F
@Load 2.25 lb
|
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 – 260 °C | 428 – 500 °F | mass temperature |
| Feed Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F | |
| Injection Velocity | 100 – 200 mm/sec | 3.94 – 7.87 in/sec | |
| Hold Pressure | 3.00 – 6.00 MPa | 435 – 870 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Emission (µgC/g) | < 50 | VDA 277 |
| Fogging (mg) | < 2 | DIN 75201;100°C, 16h |
| Screw Speed | low to medium |