Borealis Daplen™ EF210AE Polypropylene TPO Compound
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen™ EF210AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface quality and is easy to process. Applications: Daplen™ EF210AE has been developed especially for the automotive industry including bumpers, and exterior trims.Information provided by Borealis AG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | mold average;Borealis Method |
| Melt Flow | 22 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
22 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527-2 |
| Elongation at Break | 300 % | 300 % | ISO 527-2 |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1mm/min; ISO 527-2 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m²
@Temperature -20.0 °C
|
2.38 ft-lb/in²
@Temperature -4.00 °F
|
ISO 180/1A |
| 50.0 kJ/m²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Charpy Impact, Notched | 0.550 J/cm²
@Temperature -20.0 °C
|
2.62 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 6.00 J/cm²
@Temperature 23.0 °C
|
28.6 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C
@Temperature -30.0 – 80.0 °C
|
25.0 µin/in-°F
@Temperature -22.0 – 176 °F
|
Borealis Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-2 |
| Vicat Softening Point | 120 °C
@Load 1.02 kg
|
248 °F
@Load 2.25 lb
|
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 – 260 °C | 428 – 500 °F | mass temperature |
| Feed Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F | |
| Injection Velocity | 100 – 200 mm/sec | 3.94 – 7.87 in/sec | |
| Hold Pressure | 30.0 – 60.0 MPa | 4350 – 8700 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | low to medium | |
| Screw Speed | low to medium |