Diamond Polymers ASA 91802
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, High HeatInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0070 cm/cm | 0.0040 – 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
0.50 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 2.5 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
2.5 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 45.79 MPa | 6642 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.88 GPa | 418 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C |
1.90 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.8 °C | 199 °F | 0.125 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
| 100 °C | 212 °F | 0.25 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 | |
| Vicat Softening Point | 117 °C | 243 °F | 0.125 inch, 1 Kg; ASTM D1525 |