Diamond Polymers ASA S750
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: ASA Weatherable Polymer, Injection Molding Grade, Very High ImpactInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0080 cm/cm | 0.0040 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 0.90 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
0.90 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 2.7 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
2.7 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 88 | 88 | ASTM D785 |
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.88 GPa | 273 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 3.74 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C |
7.00 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 91.1 °C | 196 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 104 °C | 219 °F | 0.125 inch, 1 Kg; ASTM D1525 |