Diamond Polymers ASA TWP 155
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Transparent Weatherable PolymerInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0080 cm/cm | 0.0040 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 2.1 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
2.1 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 14 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
14 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 58.29 MPa | 8454 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.34 GPa | 339 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.6 %
@Thickness 3.00 mm
|
7.6 %
@Thickness 0.118 in
|
ASTM D1003 |
| Transmission, Visible | 85.5 %
@Thickness 3.00 mm
|
85.5 %
@Thickness 0.118 in
|
ASTM D1003 |