Diamond Polymers SAN 268 Styrene Acrylonitrile, Transparent Engineering Thermoplastic
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 – 0.0070 cm/cm | 0.0030 – 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
3.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| 10.5 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
10.5 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 73.7 MPa | 10700 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Modulus | 3.624 GPa | 525.6 ksi | chs 0.05 in/min; tangent; ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C |
0.401 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 102 °C
@Load 1.00 kg,
Thickness 3.17 mm |
216 °F
@Load 2.20 lb,
Thickness 0.125 in |
ASTM D1525 |
| Flammability, UL94 | HB
@Thickness 1.59 mm
|
HB
@Thickness 0.0625 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |