DuPont™ Surlyn® 1652-1 Zinc Ionomer Resin for Blown/Cast Film and Extrusion Coating (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Surlyn® 1652-1 is an ionomer resin available for use in blown/cast film and extrusion coating operations. It can be used in both extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, seafood and cheese packaging; Cereal liners; Medical/pharmaceutical packaging; Powdered/granular food and nonfood pouches; Edible oil, motor oil, and other liquid product pouches; Snack structuresData provided by the manufacturer, DuPont Packaging.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 4.5 g/10 min
@Load 2.16 kg,
Temperature 190 °C |
4.5 g/10 min
@Load 4.76 lb,
Temperature 374 °F |
ASTM D1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Secant Modulus, MD | 0.160 GPa | 23.2 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0450 GPa | 6.53 ksi | ASTM D882 |
| Impact | 220 | 220 | Spencer Impact in J/cm; ASTM D3420 |
| Elmendorf Tear Strength, MD | 3.50 g/micron | 88.9 g/mil | |
| Elmendorf Tear Strength, TD | 3.70 g/micron | 94.0 g/mil | |
| Dart Drop | 7.90 g/micron | 201 g/mil | ASTM D1709B |
| Seal Strength | <= 2700 g/25 mm | <= 2700 g/in | Varies with seal bar temp. |
| Hot Tack Strength | <= 2000 g/25 mm | <= 2000 g/in | Varies with seal bar temp.; Packforsk Method |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 100 °C | 212 °F | DSC; ASTM D3418 |
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.5 % | 3.5 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 20°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 177 °C | 351 °F |