Eastman Tenite 371A-10 Cellulose Acetate Propionate (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
10% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0060 in/in
@Thickness 0.126 in
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min |
| Elongation at Break | 36 % | 36 % | |
| Elongation at Yield | 4.0 % | 4.0 % | |
| Tensile Modulus | 1.74 GPa | 252 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
||
| Charpy Impact, Notched | 1.57 J/cm² | 7.47 ft-lb/in² | |
| 0.340 J/cm²
@Temperature -30.0 °C
|
1.62 ft-lb/in²
@Temperature -22.0 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 107 µm/m-°C
@Temperature 20.0 °C
|
59.4 µin/in-°F
@Temperature 68.0 °F
|
|
| CTE, linear, Transverse to Flow | 127 µm/m-°C
@Temperature 20.0 °C
|
70.6 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | |
| Vicat Softening Point | 94.0 °C | 201 °F | |
| Glass Transition Temp, Tg | 110 °C | 230 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 225 – 240 °C | 437 – 464 °F |