Eastman Tenite 572A1V95316 Cellulose Acetate Butyrate, Smoke, Trsp
| Manufacturer | Eastman Chemical |
| Trade Name | Tenite |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Applications:Molded partsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties – toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite Cellulose Acetate Butyrate 572-16 contains an odor mask lubricant and an ultra-violet inhibitor (UVI). It has a plasticizer level of 16%.Information provided by Eastman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 1.2 %
@Time 86400 sec
|
1.2 %
@Time 24.0 hour
|
Immersion; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 31.0 MPa | 4500 psi | ASTM D638 |
| Tensile Strength, Yield | 30.3 MPa | 4390 psi | ASTM D638 |
| Elongation at Break | 26 % | 26 % | ASTM D638 |
| Flexural Modulus | 1.162 GPa | 168.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.02 J/cm
@Temperature -40.0 °C
|
1.91 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 5.31 J/cm
@Temperature 23.0 °C
|
9.95 ft-lb/in
@Temperature 73.4 °F
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Formula Number | 572 | UVI; odor mask |
| Plasticizer | 16 percent | |
| Weight Loss on Heating | 0.9 percent | ASTM D707, 72 hrs, 80°C |