Elektro-Isola G-Etronax EP S Epoxy, Glass Fabric Reinforcement, Green, Sheets
| Manufacturer | Elektro-Isola |
| Trade Name | G-Etronax |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Particularly good electrical and mechanical properties by continuous use, even at high temperatures. Very good chemical resistance. Engineering and insulation material in electrical machinery, transformers and chemical plants. Suitable for mechanical applications. The flexural strength and modulus of elasticity values are measured along the sheet.Applications: Wear parts/vanes in oil-lubricated vacuum pumps.Information provided by Elektro-Isola
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1 |
| Water Absorption | 0.20 % | 0.20 % | 24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 320 MPa
@Thickness >=1.50 mm
|
46400 psi
@Thickness >=0.0591 in
|
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
| Modulus of Elasticity | 24.0 GPa
@Thickness >=1.50 mm
|
3480 ksi
@Thickness >=0.0591 in
|
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
| Flexural Strength | 375 MPa
@Thickness >=1.50 mm
|
54400 psi
@Thickness >=0.0591 in
|
1hr/180°C/measured at 180°C; ISO 178; IEC/EN 60893-2 5.1 |
| 500 MPa
@Thickness >=1.50 mm
|
72500 psi
@Thickness >=0.0591 in
|
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 | |
| Compressive Strength | 600 MPa
@Thickness >=5.00 mm
|
87000 psi
@Thickness >=0.197 in
|
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
| Shear Strength | 60.0 MPa
@Thickness >=5.00 mm
|
8700 psi
@Thickness >=0.197 in
|
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
| Izod Impact, Notched (ISO) | 80.0 kJ/m²
@Thickness >=5.00 mm
|
38.1 ft-lb/in²
@Thickness >=0.197 in
|
24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 200 °C
@Thickness 0.000 mm,
Time 7.20e+7 sec |
392 °F
@Thickness 0.000 in,
Time 20000 hour |
IEC 60216; IEC/EN 60893-2 7.1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | 2.00e+11 ohm
@Thickness >=3.00 mm
|
2.00e+11 ohm
@Thickness >=0.118 in
|
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3 |
| Dielectric Constant | 5.0
@Thickness <=3.00 mm,
Frequency 50.0 Hz |
5.0
@Thickness <=0.118 in,
Frequency 50.0 Hz |
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| 5.0
@Thickness <=3.00 mm,
Frequency 1.00e+6 Hz |
5.0
@Thickness <=0.118 in,
Frequency 1.00e+6 Hz |
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 | |
| Dielectric Strength | 3.20 kV/mm
@Thickness >=3.00 mm
|
81.3 kV/in
@Thickness >=0.118 in
|
24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2 |
| 18.0 kV/mm
@Thickness 3.00 mm
|
457 kV/in
@Thickness 0.118 in
|
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1 | |
| Dissipation Factor | 0.0080
@Frequency 50.0 Hz
|
0.0080
@Frequency 50.0 Hz
|
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| 0.010
@Frequency 1.00e+6 Hz
|
0.010
@Frequency 1.00e+6 Hz
|
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 | |
| Comparative Tracking Index | 400 V
@Thickness 3.00 mm
|
400 V
@Thickness 0.118 in
|
IEC 60112; IEC/EN 60893-2 6.4 |