Eurotec® Tecomid® NT40 GR30 NL HS PPA, 30% glass fiber reinforced, heat stabilized, natural
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.70 %
@Temperature 23.0 °C
|
1.70 %
@Temperature 73.4 °F
|
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m²
@Temperature -30.0 °C
|
4.76 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1A |
| 11.0 kJ/m²
@Temperature 23.0 °C
|
5.23 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 315 °C | 599 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 305 °C | 581 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75 |
| Vicat Softening Point | 290 °C
@Load 5.10 kg
|
554 °F
@Load 11.2 lb
|
ISO 306 |
| Flammability, UL94 | HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
|
| HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 320 – 340 °C | 608 – 644 °F | |
| Feed Temperature | 60.0 – 80.0 °C | 140 – 176 °F | Throat |
| Mold Temperature | 140 – 180 °C | 284 – 356 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 40.0 – 80.0 MPa | 5800 – 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |