ExxonMobil Escorene® LD 767.MJ Molding, extrusion and compounding resin (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Escorene Ultra LD 767.MJ is a high viscosity, 29.5% vinyl acetate copolymer suitable for making very soft, blow molded or extruded articles with very good low temperature toughness. It can also be used as a polymer modifier to make specialty compounds.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 29.5 % | 29.5 % | ExxonMobil Method |
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 74 | 74 | 15s; ASTM D2240 |
| Hardness, Shore D | 26 | 26 | 15s; ASTM D2240 |
| Tensile Strength at Break | 9.58 MPa | 1390 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0241 GPa | 3.49 ksi | 1% secant; ASTM D790 |
| Impact Test | 16.3 J
@Temperature 23.0 °C
|
12.0 ft-lb
@Temperature 73.4 °F
|
Instrument Impact, Total Energy; ASTM D3763 |
| 38.0 J
@Temperature -40.0 °C
|
28.0 ft-lb
@Temperature -40.0 °F
|
Instrumented Impact, Total Energy; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 69.4 °C | 157 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 43.9 °C | 111 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |