ExxonMobil OPTEMA™ TC 115 Blown Film Resin (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
OPTEMA TC 115 is an ethylene methyl acrylate copolymer, designed for specialty blown film applications. It yields soft, elastic films.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | ExxonMobil Method |
| Methyl Acrylate Content | 16.5 % | 16.5 % | |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 370 % | 370 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.787 g/micron | 20.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.94 g/micron | 100 g/mil | ASTM D1922 |
| Dart Drop | 10.2 g/micron | 260 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 24.2 MPa | 3510 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.2 MPa | 3660 psi | ASTM D882 |
| 1% Secant Modulus, MD | 64.3 MPa | 9320 psi | ASTM D882 |
| 1% Secant Modulus, TD | 60.4 MPa | 8760 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 88.9 °C | 192 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 63.9 °C | 147 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |