Gharda Chemicals GATONE™ 5700 Polyetheretherketone (PEEK) (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric Strength, Volume Resistivity, Tracking Resistance Excellent Radiation Resistance Applications:Medical appliances including implantationAerospace applicationEngineering applications like compressor plates, valve seats, moving parts for textile machines Electrical and communication cables Scientific laboratory instruments Information provided by Gharda ChemicalsSolvay Advanced Polymers completed its acquisition of this product line in May 2006.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 Hours; ASTM D570 |
| Melt Flow | 45.5 – 91 g/10 min
@Load 5.00 kg,
Temperature 380 °C |
45.5 – 91 g/10 min
@Load 11.0 lb,
Temperature 716 °F |
6`; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790 |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C
@Temperature 20.0 °C
|
25.0 µin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Use; UL-746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ASTM D648 |
| Glass Transition Temp, Tg | 148 °C | 298 °F | ASTM D3482 |
| Flammability, UL94 | V-0
@Thickness 3.20 mm
|
V-0
@Thickness 0.126 in
|
UL 94 |
| Oxygen Index | 40 % | 40 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 2.8
@Frequency 60 Hz
|
2.8
@Frequency 60 Hz
|
ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0030
@Frequency 60 Hz
|
0.0030
@Frequency 60 Hz
|
ASTM D150 |
| Comparative Tracking Index | 150 V | 150 V | ASTM D3638 |