Huntsman IROGRAN® A 80 P 5039 TPU-Polyether
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Hardness, Shore D | 29 | 29 | ASTM D2240 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN 53504 |
| Elongation at Break | 760 % | 760 % | ASTM D412 |
| 100% Modulus | 0.00460 GPa | 0.667 ksi | DIN 53504 |
| 300% Modulus | 0.00870 GPa | 1.26 ksi | DIN 53504 |
| Rebound | 47 % | 47 % | Bayshore; ASTM D2632 |
| Tear Strength | 84.1 kN/m | 480 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 23 %
@Temperature 23.0 °C,
Time 252000 sec |
23 %
@Temperature 73.4 °F,
Time 70.0 hour |
ASTM D395 |
| 43 %
@Temperature 70.0 °C,
Time 86400 sec |
43 %
@Temperature 158 °F,
Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 – 155 °C | 293 – 311 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |