Idemitsu Kosan Xarec® N WA 7010 SPS, 10% Glass Filled (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Crystalline Polymer Blend, Glass Filled. Used in Automotive Electronics applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Filler Content | 10 % | 10 % | Glass |
| Moisture Absorption | 0.450 % | 0.450 % | 24 hours, 50% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm
@Thickness 2.00 mm
|
0.0055 in/in
@Thickness 0.0787 in
|
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.80 GPa | 696 ksi | ASTM D638 |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D790 |
| Flexural Modulus | 6.90 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 3.70 kJ/m²
@Temperature 23.0 °C
|
1.76 ft-lb/in²
@Temperature 73.4 °F
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 – 320 °C | 554 – 608 °F | |
| Mold Temperature | 60.0 – 80.0 °C | 140 – 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F |