Idemitsu Kosan Xarec® EA 543 SPS, 40% Glass Filled
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | |
| Filler Content | 40 % | 40 % | |
| Water Absorption | 0.020 % | 0.020 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm | 0.0010 – 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 – 0.0070 cm/cm | 0.0030 – 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | |
| Elongation at Break | 1.6 % | 1.6 % | |
| Tensile Modulus | 12.9 GPa | 1870 ksi | |
| Flexural Yield Strength | 200 MPa | 29000 psi | |
| Flexural Modulus | 13.1 GPa | 1900 ksi | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | |
| Charpy Impact Unnotched | 2.90 J/cm² | 13.8 ft-lb/in² | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.0 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
8.89 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
|
| CTE, linear, Transverse to Flow | 29.0 µm/m-°C | 16.1 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| UL RTI, Electrical | 125 °C | 257 °F | UL746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL746B |
| Flammability, UL94 | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.5 | 3.5 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D145 |
| Dissipation Factor | 0.0030 | 0.0030 | IEC 60250 |
| Arc Resistance | 60 – 120 sec | 60 – 120 sec | ASTM D495 |
| Comparative Tracking Index | 250 – 400 V | 250 – 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | >= 120 sec
@Thickness 1.50 mm
|
>= 120 sec
@Thickness 0.0591 in
|
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs
@Thickness 1.50 mm
|
>= 120 arcs
@Thickness 0.0591 in
|
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 – 10.0 mm/min | 0.000 – 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 – 310 °C | 536 – 590 °F | |
| Mold Temperature | 50.0 – 80.0 °C | 122 – 176 °F | |
| 130 – 155 °C | 266 – 311 °F | For optimal surface finish |