Idemitsu Kosan Xarec® WA 210 SPS, 20% Glass Filled
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Crystalline Polymer, Glass Filled, Impact Modified, Improved Mold Release. Used in Automotive and Industrial applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | |
| Filler Content | 20 % | 20 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0040 cm/cm | 0.0020 – 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 – 0.0050 cm/cm | 0.0030 – 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | |
| Elongation at Break | 2.3 % | 2.3 % | |
| Tensile Modulus | 7.30 GPa | 1060 ksi | |
| Flexural Yield Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 7.00 GPa | 1020 ksi | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
15.0 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
|
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C | 32.2 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL746B |
| Flammability, UL94 | HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D145 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 |
| Arc Resistance | 120 – 180 sec | 120 – 180 sec | ASTM D495 |
| Comparative Tracking Index | 250 – 400 V | 250 – 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | 15 – 30 sec
@Thickness 1.50 mm
|
15 – 30 sec
@Thickness 0.0591 in
|
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs
@Thickness 1.50 mm
|
>= 120 arcs
@Thickness 0.0591 in
|
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 – 10.0 mm/min | 0.000 – 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 – 310 °C | 536 – 590 °F | |
| Mold Temperature | 50.0 – 80.0 °C | 122 – 176 °F | |
| 130 – 155 °C | 266 – 311 °F | For optimal surface finish |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | NSF61 |