Idemitsu Kosan Xarec® WA 212LG SPS, 30% Glass Filled
| Manufacturer | Idemitsu Kosan Co., Ltd. |
| Trade Name | Xarec® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.010 % | 0.010 % | 24 hrs., 50% RH |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0040 cm/cm | 0.0010 – 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0030 – 0.0070 cm/cm | 0.0030 – 0.0070 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | |
| Elongation at Break | 2.2 % | 2.2 % | |
| Tensile Modulus | 9.40 GPa | 1360 ksi | |
| Flexural Yield Strength | 190 MPa | 27600 psi | |
| Flexural Modulus | 9.20 GPa | 1330 ksi | |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
11.7 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
|
| CTE, linear, Transverse to Flow | 57.0 µm/m-°C | 31.7 µin/in-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 265 °C | 509 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL746B |
| Flammability, UL94 | HB
@Thickness 0.750 mm
|
HB
@Thickness 0.0295 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | |
| Dielectric Constant | 3.1 | 3.1 | |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | ASTM D145 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 60250 |
| Arc Resistance | 120 – 180 sec | 120 – 180 sec | ASTM D495 |
| Comparative Tracking Index | 250 – 400 V | 250 – 400 V | IEC 60112 |
| Hot Wire Ignition, HWI | 30 – 60 sec
@Thickness 1.50 mm
|
30 – 60 sec
@Thickness 0.0591 in
|
UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs
@Thickness 1.50 mm
|
>= 120 arcs
@Thickness 0.0591 in
|
UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 – 10.0 mm/min | 0.000 – 0.394 in/min | UL746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 – 310 °C | 536 – 590 °F | |
| Mold Temperature | 50.0 – 80.0 °C | 122 – 176 °F | |
| 130 – 155 °C | 266 – 311 °F | For optimal surface finish |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Comments | low outgassing @ elevated temperatures | |
| No mold release |