Ineos ABS Cadon® 127 SMA General Purpose, High Heat (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Bayer Corporation, Plastics DivisionLANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS. This product is no longer listed as a standard NAFTA product.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 – 0.0070 cm/cm | 0.0050 – 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
2.0 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Tensile Modulus | 2.10 GPa | 305 ksi | ASTM D638 |
| Flexural Yield Strength | 66.0 MPa | 9570 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm
@Temperature -40.0 °C
|
1.87 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 2.10 J/cm
@Thickness 3.17 mm
|
3.93 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C
@Temperature 20.0 °C
|
38.9 µin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C
@Thickness 13.0 mm
|
248 °F
@Thickness 0.512 in
|
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C
@Thickness 13.0 mm
|
234 °F
@Thickness 0.512 in
|
ASTM D648 |
| Vicat Softening Point | 131 °C | 268 °F | Rate B; ASTM D1525 |
| UL RTI, Electrical | 100 °C
@Thickness 1.60 mm
|
212 °F
@Thickness 0.0630 in
|
UL746B |
| UL RTI, Mechanical with Impact | 95.0 °C
@Thickness 1.60 mm
|
203 °F
@Thickness 0.0630 in
|
UL746B |
| UL RTI, Mechanical without Impact | 95.0 °C
@Thickness 1.60 mm
|
203 °F
@Thickness 0.0630 in
|
UL746B |
| Flammability, UL94 | HB
@Thickness 1.57 mm
|
HB
@Thickness 0.0618 in
|
|
| HB
@Thickness 1.57 mm
|
HB
@Thickness 0.0618 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 – 280 °C | 482 – 536 °F |