Ineos ABS Centrex® 811 ASA Blend (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Melt Flow | 9.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
9.0 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
cm³/10 min. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | |
| Elongation at Break | 45 % | 45 % | Nominal |
| Elongation at Yield | 3.0 % | 3.0 % | |
| Tensile Modulus | 2.07 GPa | 300 ksi | |
| Charpy Impact, Notched | 4.59 J/cm² | 21.8 ft-lb/in² | |
| 0.290 J/cm²
@Temperature -30.0 °C
|
1.38 ft-lb/in²
@Temperature -22.0 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 119 µm/m-°C
@Temperature 20.0 °C
|
66.1 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | |
| Vicat Softening Point | 94.0 °C | 201 °F | 50°C/h 50N |
| Flammability, UL94 | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
UL Recognized |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
UL Recognized |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection Molding |
| Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | |
| Injection Pressure | 60.0 MPa | 8700 psi |