Ineos ABS Lustran® SAN DN59 SAN, Soft-Flow Grade
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Lustran® SAN DN59 resin is a soft-flow grade of transparent SAN (styrene acrylonitrile) thermoplastic. It has been designed for use in compounding and thin-wall injection molded applications. Lustran® SAN DN59 has a large molding window and is easy to process. It is available only in natural (000000) color.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM-D792 |
| Linear Mold Shrinkage | 0.0030 – 0.0040 cm/cm | 0.0030 – 0.0040 in/in | ASTM-D955 |
| Melt Flow | 25 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
25 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ISO 527 |
| Tensile Modulus | 4.71 GPa | 683 ksi | ISO 527 |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | ISO 178 |
| Flexural Modulus | 3.76 GPa | 545 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.47 kJ/m² | 0.699 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 99.5 °C
@Load 5.00 kg
|
211 °F
@Load 11.0 lb
|
Method B, 50°C/hour; ISO 306 |
| 101.8 °C
@Load 5.00 kg
|
215.2 °F
@Load 11.0 lb
|
Method B, 120°C/hour; ISO 306 | |
| 105.9 °C
@Load 5.00 kg
|
222.6 °F
@Load 11.0 lb
|
Method A, 120°C/hour; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 170 – 185 °C | 338 – 365 °F | Injection Molding |
| Middle Barrel Temperature | 185 – 200 °C | 365 – 392 °F | Injection Molding |
| Front Barrel Temperature | 200 – 215 °C | 392 – 419 °F | Injection Molding |
| Nozzle Temperature | 200 – 215 °C | 392 – 419 °F | Injection Molding |
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | Injection Molding |
| Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | Injection Molding |
| Drying Temperature | 71.0 – 77.0 °C
@Time 14400 sec
|
160 – 171 °F
@Time 4.00 hour
|
|
| 82.0 – 88.0 °C
@Time 7200 sec
|
180 – 190 °F
@Time 2.00 hour
|
||
| Moisture Content | <= 0.20 % | <= 0.20 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Injection Pressure | 68.9 – 138 MPa | 10000 – 20000 psi | Injection Molding |
| Back Pressure | 0.000 – 0.172 MPa | 0.000 – 25.0 psi | Injection Molding |
| Clamp Pressure | 30.8 – 61.6 MPa | 4470 – 8930 psi | Injection Molding |
| Cushion | <= 0.317 cm | <= 0.125 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acrylonitrile Content (%) | 29.5 | |
| Hold Pressure | 40-80% of Injection Pressure, Injection Molding | |
| Injection Speed | Moderate to High | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.7 | Injection Molding |