Inno-Comp INNOPOL® CS 2-9514 10% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
INNOPOL® CS 2-9514 is a 10% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9514 is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc
@Temperature 23.0 °C
|
0.0350 lb/in³
@Temperature 73.4 °F
|
ISO 1183 |
| Melt Flow | 60 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
60 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.5 MPa | 2830 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 7.5 % | 7.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.15 GPa | 167 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.30 GPa | 189 ksi | 2 mm/min; ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm²
@Temperature -20.0 °C
|
2.38 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| 3.50 J/cm²
@Temperature 23.0 °C
|
16.7 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75-1,-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural |