IRPC Polimaxx Polene HI830 Polystyrene
| Manufacturer | IRPC Polimaxx |
| Trade Name | Polene |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
APPLICATIONS: EXTRUSION APPLICATION, VACUUM SHEET : FOOD PACKAGING ELECTRICAL APPLIANCES, HOUSEHOLD PRODUCT, TOYS, SANITARY, etc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
3.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 82
@Thickness 6.35 mm,
Temperature 23.0 °C |
82
@Thickness 0.250 in,
Temperature 73.4 °F |
ASTM D785 |
| Tensile Strength, Yield | 21.4 MPa
@Temperature 23.0 °C
|
3100 psi
@Temperature 73.4 °F
|
ASTM D638 |
| Flexural Yield Strength | 41.4 MPa
@Temperature 23.0 °C
|
6000 psi
@Temperature 73.4 °F
|
ASTM D790 |
| Flexural Modulus | 2.14 GPa
@Temperature 23.0 °C
|
310 ksi
@Temperature 73.4 °F
|
ASTM D790 |
| Izod Impact, Notched | 0.120 J/cm
@Thickness 6.35 mm,
Temperature 23.0 °C |
0.225 ft-lb/in
@Thickness 0.250 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C
@Thickness 6.35 mm
|
194 °F
@Thickness 0.250 in
|
ASTM D648 |
| Vicat Softening Point | 96.0 °C
@Load 1.00 kg,
Thickness 3.17 mm |
205 °F
@Load 2.20 lb,
Thickness 0.125 in |
ASTM D1525 |
| Flammability, UL94 | HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 190 – 230 °C | 374 – 446 °F | extrusion |
| Drying Temperature | 80.0 – 85.0 °C
@Time 7200 – 10800 sec
|
176 – 185 °F
@Time 2.00 – 3.00 hour
|