LATI Latene® 7 TR-V2 PP Homopolymer, Mineral Reinforced, Flame Retardant
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polypropylene homopolymer (PPh) based compound. Mineral filler. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free. Good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0135 – 0.0165 cm/cm | 0.0135 – 0.0165 in/in | |
| Linear Mold Shrinkage, Transverse | 0.014 – 0.017 cm/cm | 0.014 – 0.017 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | |
| Elongation at Break | 25 %
@Temperature 23.0 °C
|
25 %
@Temperature 73.4 °F
|
|
| >= 100 %
@Temperature 60.0 °C
|
>= 100 %
@Temperature 140 °F
|
||
| >= 100 %
@Temperature 90.0 °C
|
>= 100 %
@Temperature 194 °F
|
||
| Elongation at Yield | 6.0 %
@Temperature 23.0 °C
|
6.0 %
@Temperature 73.4 °F
|
|
| 8.0 %
@Temperature 60.0 °C
|
8.0 %
@Temperature 140 °F
|
||
| 9.0 %
@Temperature 90.0 °C
|
9.0 %
@Temperature 194 °F
|
||
| Tensile Modulus | 0.550 GPa
@Temperature 90.0 °C
|
79.8 ksi
@Temperature 194 °F
|
|
| 0.950 GPa
@Temperature 60.0 °C
|
138 ksi
@Temperature 140 °F
|
||
| 2.20 GPa
@Temperature 23.0 °C
|
319 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 1.50 J/cm²
@Temperature -20.0 °C
|
7.14 ft-lb/in²
@Temperature -4.00 °F
|
|
| 5.00 J/cm²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.0300 J/cm²
@Temperature -20.0 °C
|
0.143 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.150 J/cm²
@Temperature 23.0 °C
|
0.714 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | |
| Vicat Softening Point | 100 °C
@Load 5.00 kg
|
212 °F
@Load 11.0 lb
|
|
| Flammability, UL94 | V-2
@Thickness 3.00 mm
|
V-2
@Thickness 0.118 in
|
|
| V-2
@Thickness 1.50 mm
|
V-2
@Thickness 0.0591 in
|
||
| V-2
@Thickness 0.750 mm
|
V-2
@Thickness 0.0295 in
|
||
| Oxygen Index | 29 % | 29 % | |
| Glow Wire Test | 960 °C
@Thickness 1.00 mm
|
1760 °F
@Thickness 0.0394 in
|
GWFI/GWT |
| 960 °C
@Thickness 2.00 mm
|
1760 °F
@Thickness 0.0787 in
|
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 – 220 °C | 356 – 428 °F | |
| Mold Temperature | 20.0 – 40.0 °C | 68.0 – 104 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |