LATI Latene® AG9H MI/40 PP Homopolymer, 40% Mica Reinforced, Heat Stabilized
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Mica filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0080 – 0.0105 cm/cm | 0.0080 – 0.0105 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 – 0.011 cm/cm | 0.0080 – 0.011 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 5.00 MPa
@Temperature 90.0 °C
|
725 psi
@Temperature 194 °F
|
|
| 15.0 MPa
@Temperature 60.0 °C
|
2180 psi
@Temperature 140 °F
|
||
| 25.0 MPa
@Temperature 23.0 °C
|
3630 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 3.0 %
@Temperature 23.0 °C
|
3.0 %
@Temperature 73.4 °F
|
|
| 5.0 %
@Temperature 60.0 °C
|
5.0 %
@Temperature 140 °F
|
||
| 20 %
@Temperature 90.0 °C
|
20 %
@Temperature 194 °F
|
||
| Elongation at Yield | 2.0 %
@Temperature 23.0 °C
|
2.0 %
@Temperature 73.4 °F
|
|
| 3.0 %
@Temperature 60.0 °C
|
3.0 %
@Temperature 140 °F
|
||
| 3.5 %
@Temperature 90.0 °C
|
3.5 %
@Temperature 194 °F
|
||
| Tensile Modulus | 1.20 GPa
@Temperature 90.0 °C
|
174 ksi
@Temperature 194 °F
|
|
| 2.50 GPa
@Temperature 60.0 °C
|
363 ksi
@Temperature 140 °F
|
||
| 4.20 GPa
@Temperature 23.0 °C
|
609 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 0.800 J/cm²
@Temperature -20.0 °C
|
3.81 ft-lb/in²
@Temperature -4.00 °F
|
|
| 1.00 J/cm²
@Temperature 23.0 °C
|
4.76 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.100 J/cm²
@Temperature -20.0 °C
|
0.476 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.150 J/cm²
@Temperature 23.0 °C
|
0.714 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 110 °C
@Load 5.00 kg
|
230 °F
@Load 11.0 lb
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 240 °C | 392 – 464 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |