LATI Laticonther 57 CPG/550 PPA, Glass Fiber Reinforced
| Manufacturer | LATI |
| Trade Name | Laticonther |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
High thermal conductivity product based on Semi-aromatic polyamide (PPA). Special filler. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.99 g/cc | 0.0719 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 – 0.0045 cm/cm | 0.0030 – 0.0045 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0050 – 0.0065 cm/cm | 0.0050 – 0.0065 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | |
| Elongation at Break | 0.60 % | 0.60 % | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.20 W/m-K | 8.33 BTU-in/hr-ft²-°F | Longitudinal |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| Vicat Softening Point | 100 °C
@Load 5.00 kg
|
212 °F
@Load 11.0 lb
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 310 – 330 °C | 590 – 626 °F | |
| Mold Temperature | 140 – 160 °C | 284 – 320 °F | |
| Drying Temperature | 120 – 130 °C
@Time 10800 sec
|
248 – 266 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |