LATI Latigloss 57 G/60 F2 PPA, 60% Glass Fiber Reinforced
| Manufacturer | LATI |
| Trade Name | Latigloss |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact application. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0015 – 0.0025 cm/cm | 0.0015 – 0.0025 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0025 – 0.0045 cm/cm | 0.0025 – 0.0045 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa
@Temperature 150 °C
|
10200 psi
@Temperature 302 °F
|
|
| 130 MPa
@Temperature 120 °C
|
18900 psi
@Temperature 248 °F
|
||
| 210 MPa
@Temperature 90.0 °C
|
30500 psi
@Temperature 194 °F
|
||
| 250 MPa
@Temperature 60.0 °C
|
36300 psi
@Temperature 140 °F
|
||
| 290 MPa
@Temperature 23.0 °C
|
42100 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 1.6 %
@Temperature 23.0 °C
|
1.6 %
@Temperature 73.4 °F
|
|
| 1.7 %
@Temperature 60.0 °C
|
1.7 %
@Temperature 140 °F
|
||
| 1.9 %
@Temperature 90.0 °C
|
1.9 %
@Temperature 194 °F
|
||
| 3.0 %
@Temperature 120 °C
|
3.0 %
@Temperature 248 °F
|
||
| 4.5 %
@Temperature 150 °C
|
4.5 %
@Temperature 302 °F
|
||
| Tensile Modulus | 6.00 GPa
@Temperature 150 °C
|
870 ksi
@Temperature 302 °F
|
|
| 15.5 GPa
@Temperature 120 °C
|
2250 ksi
@Temperature 248 °F
|
||
| 21.5 GPa
@Temperature 90.0 °C
|
3120 ksi
@Temperature 194 °F
|
||
| 23.5 GPa
@Temperature 60.0 °C
|
3410 ksi
@Temperature 140 °F
|
||
| 25.0 GPa
@Temperature 23.0 °C
|
3630 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 285 °C | 545 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | |
| Vicat Softening Point | 260 °C
@Load 5.00 kg
|
500 °F
@Load 11.0 lb
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 310 – 340 °C | 590 – 644 °F | |
| Mold Temperature | 150 – 170 °C | 302 – 338 °F | |
| Drying Temperature | 120 – 130 °C
@Time 10800 sec
|
248 – 266 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |