LATI Latiohm 85-06 PD01 G/15 PES, 15% Glass Fiber Reinforced
| Manufacturer | LATI |
| Trade Name | Latiohm |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Semiconductive/dissipative product based on Polyether Sulfone (PES). Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0025 cm/cm | 0.0010 – 0.0025 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0025 – 0.0045 cm/cm | 0.0025 – 0.0045 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | |
| Elongation at Break | 1.5 % | 1.5 % | |
| Tensile Modulus | 13.8 GPa | 2000 ksi | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |
| Vicat Softening Point | 215 °C
@Load 5.00 kg
|
419 °F
@Load 11.0 lb
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 200 ohm-cm | 200 ohm-cm | |
| Surface Resistance | 200 ohm | 200 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 350 – 390 °C | 662 – 734 °F | |
| Mold Temperature | 150 – 190 °C | 302 – 374 °F | |
| Drying Temperature | 150 – 180 °C
@Time 10800 sec
|
302 – 356 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |