LATI Latistat 52/7-02 MI/30 PP Homopolymer, 30% Mica Filled
| Manufacturer | LATI |
| Trade Name | Latistat |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Dissipative product based on Polypropylene homopolymer (PPh). Mica filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0080 – 0.010 cm/cm | 0.0080 – 0.010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0085 – 0.0105 cm/cm | 0.0085 – 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Elongation at Yield | 1.5 % | 1.5 % | |
| Tensile Modulus | 5.20 GPa | 754 ksi | |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.100 J/cm² | 0.476 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
| Vicat Softening Point | 110 °C
@Load 5.00 kg
|
230 °F
@Load 11.0 lb
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 800 ohm | 800 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 240 °C | 392 – 464 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |