Lehmann & Voss LUVOCOM® 1100-8326 Polyether sulfone, with carbon fiber, PTFE, lubricant modified
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Low warpage.Improved friction and wear behaviour. Emergency running property.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 – 0.0040 cm/cm | 0.0020 – 0.0040 in/in | |
| Melt Flow | <= 15.3 g/10 min
@Load 5.00 kg,
Temperature 345 °C |
<= 15.3 g/10 min
@Load 11.0 lb,
Temperature 653 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 91.0 MPa | 13200 psi | |
| Elongation at Yield | 1.7 % | 1.7 % | |
| 2.2 % | 2.2 % | flexural | |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | |
| Flexural Strength | 137 MPa | 19900 psi | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | DIN 53752 |
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 200 °C | 392 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1e+05 | <= 1e+05 | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 – 360 °C | 644 – 680 °F | |
| Zone 1 | 355 – 375 °C | 671 – 707 °F | |
| Zone 2 | 360 – 380 °C | 680 – 716 °F | |
| Zone 3 | 350 – 370 °C | 662 – 698 °F | |
| Mold Temperature | 120 – 200 °C | 248 – 392 °F | |
| Drying Temperature | 150 °C
@Time 10800 – 18000 sec
|
302 °F
@Time 3.00 – 5.00 hour
|
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |