LG Chemical 40 AF Flame Retardant HIPS
| Manufacturer |
Material Notes:
High impact, Safety standards: listed with UL CSA, and classified according to IEC 707, Meet requirements for flammability, mechanical and electrical properties, Applications include televisions, VTR, monitors, computers and other electrical electronic parts requiring flame retard
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0080 cm/cm | 0.0040 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 9.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
9.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 26.5 MPa | 3840 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 41.2 MPa | 5980 psi | 15 mm/min; ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 15 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm
@Thickness 6.35 mm
|
1.46 ft-lb/in
@Thickness 0.250 in
|
ASTM D256 |
| 1.13 J/cm
@Thickness 3.17 mm
|
2.12 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C
@Thickness 12.7 mm
|
171 °F
@Thickness 0.500 in
|
Unannealed; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | 1000 g; ASTM D1525 |
| Flammability, UL94 | V-0 | V-0 | 1/8 in |
| V-0 | V-0 | 1/16 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 – 120 sec | 60 – 120 sec | UL Rating PLC 6 (60-120 sec) |
| Comparative Tracking Index | 250 – 400 V | 250 – 400 V | UL Rating PLC 2 |
| Hot Wire Ignition, HWI | 15 – 30 sec | 15 – 30 sec | UL Rating PLC 3 (15-30 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 – 25.4 mm/min | 0.394 – 1.00 in/min | UL Rating PLC 1 (10-25.4 mm/min) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| IEC 707 Flammability | FVO mm/min. | 1/16 in |
Description
Material Notes:
High impact, Safety standards: listed with UL CSA, and classified according to IEC 707, Meet requirements for flammability, mechanical and electrical properties, Applications include televisions, VTR, monitors, computers and other electrical electronic parts requiring flame retard
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0080 cm/cm | 0.0040 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 9.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
9.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 26.5 MPa | 3840 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 41.2 MPa | 5980 psi | 15 mm/min; ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 15 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm
@Thickness 6.35 mm
|
1.46 ft-lb/in
@Thickness 0.250 in
|
ASTM D256 |
| 1.13 J/cm
@Thickness 3.17 mm
|
2.12 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C
@Thickness 12.7 mm
|
171 °F
@Thickness 0.500 in
|
Unannealed; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | 1000 g; ASTM D1525 |
| Flammability, UL94 | V-0 | V-0 | 1/8 in |
| V-0 | V-0 | 1/16 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 – 120 sec | 60 – 120 sec | UL Rating PLC 6 (60-120 sec) |
| Comparative Tracking Index | 250 – 400 V | 250 – 400 V | UL Rating PLC 2 |
| Hot Wire Ignition, HWI | 15 – 30 sec | 15 – 30 sec | UL Rating PLC 3 (15-30 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 – 25.4 mm/min | 0.394 – 1.00 in/min | UL Rating PLC 1 (10-25.4 mm/min) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| IEC 707 Flammability | FVO mm/min. | 1/16 in |