LG Chemical 402 AF Flame Retardant HIPS
| Manufacturer | LG Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
NON-DECA, Flame retardant, Safety standards: listed with UL CSA, and classified according to IEC 707, Meet requirements for flammability, mechanical and electrical properties, Applications include televisions, VTR, monitors, computers and other electrical electronic parts requiring flame retard
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0080 cm/cm | 0.0040 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
10 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 27.5 MPa | 3990 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 46.2 MPa | 6700 psi | 15 mm/min; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 15 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.740 J/cm
@Thickness 6.35 mm
|
1.39 ft-lb/in
@Thickness 0.250 in
|
ASTM D256 |
| 1.03 J/cm
@Thickness 3.17 mm
|
1.93 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C
@Thickness 12.7 mm
|
169 °F
@Thickness 0.500 in
|
Unannealed; ASTM D648 |
| Vicat Softening Point | 94.0 °C | 201 °F | 1000 g; ASTM D1525 |
| Flammability, UL94 | V-2 | V-2 | 1/8 in |
| V-2 | V-2 | 1/16 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 – 180 sec | 120 – 180 sec | UL Rating PLC 5 (120-180 sec) |
| Comparative Tracking Index | 400 – 600 V | 400 – 600 V | UL Rating PLC 1 (400-600 volts) |
| Hot Wire Ignition, HWI | 15 – 30 sec | 15 – 30 sec | UL Rating PLC 3 (15-30 sec) |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL Rating PLC 0 (>120 arcs) |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 – 25.4 mm/min | 0.394 – 1.00 in/min | UL Rating PLC 1 (10-25.4 mm/min) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| IEC 707 Flammability | FV2 mm/min. | 1/16 in |