LG Chemical ALPHALAC SF510 HIPS
| Manufacturer | LG Chemical |
| Trade Name | ALPHALAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Super flow, High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include TV cabinets, thin part, and high speed injection moldingCAS No. 9003-55-8Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Melt Flow | 12 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
12 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238(G) |
| 34 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
34 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238(I) | |
| 137 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
137 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238(G) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Yield | 26.5 MPa
@Thickness 3.20 mm
|
3840 psi
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Break | 51 %
@Thickness 3.20 mm
|
51 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Yield | 5.0 %
@Thickness 3.20 mm
|
5.0 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Tensile Modulus | 2.11 GPa
@Thickness 3.20 mm
|
306 ksi
@Thickness 0.126 in
|
1mm/min; ASTM D638 |
| Flexural Yield Strength | 42.2 MPa
@Thickness 3.20 mm
|
6120 psi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Flexural Modulus | 2.30 GPa
@Thickness 3.20 mm
|
334 ksi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm
@Thickness 6.50 mm,
Temperature -30.0 °C |
0.918 ft-lb/in
@Thickness 0.256 in,
Temperature -22.0 °F |
ASTM D256 |
| 0.686 J/cm
@Thickness 3.20 mm,
Temperature -30.0 °C |
1.29 ft-lb/in
@Thickness 0.126 in,
Temperature -22.0 °F |
ASTM D256 | |
| 0.981 J/cm
@Thickness 6.50 mm,
Temperature 23.0 °C |
1.84 ft-lb/in
@Thickness 0.256 in,
Temperature 73.4 °F |
ASTM D256 | |
| 1.37 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
2.57 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C
@Thickness 6.40 mm
|
192 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C
@Thickness 6.40 mm
|
176 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Vicat Softening Point | 88.0 °C
@Load 5.00 kg
|
190 °F
@Load 11.0 lb
|
50°C/h; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C
@Thickness >=1.50 mm
|
122 °F
@Thickness >=0.0591 in
|
|
| 50.0 °C
@Thickness >=3.00 mm
|
122 °F
@Thickness >=0.118 in
|
||
| UL RTI, Mechanical with Impact | 50.0 °C
@Thickness >=1.50 mm
|
122 °F
@Thickness >=0.0591 in
|
|
| 50.0 °C
@Thickness >=3.00 mm
|
122 °F
@Thickness >=0.118 in
|
||
| UL RTI, Mechanical without Impact | 50.0 °C
@Thickness >=1.50 mm
|
122 °F
@Thickness >=0.0591 in
|
|
| 50.0 °C
@Thickness >=3.00 mm
|
122 °F
@Thickness >=0.118 in
|
||
| Flammability, UL94 | HB
@Thickness >=1.50 mm
|
HB
@Thickness >=0.0591 in
|
|
| HB
@Thickness >=3.00 mm
|
HB
@Thickness >=0.118 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 – 120 sec | 60 – 120 sec | ASTM D495 |
| Comparative Tracking Index | 400 – 600 V | 400 – 600 V | |
| Hot Wire Ignition, HWI | 7.0 – 15 sec
@Thickness >=1.50 mm
|
7.0 – 15 sec
@Thickness >=0.0591 in
|
|
| 15 – 30 sec
@Thickness >=3.00 mm
|
15 – 30 sec
@Thickness >=0.118 in
|
||
| High Amp Arc Ignition, HAI | 60 – 120 arcs
@Thickness 1.50 mm
|
60 – 120 arcs
@Thickness 0.0591 in
|
|
| 60 – 120 arcs
@Thickness 3.00 mm
|
60 – 120 arcs
@Thickness 0.118 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 170 – 190 °C | 338 – 374 °F | Injection Molding |
| Middle Barrel Temperature | 180 – 200 °C | 356 – 392 °F | Injection Molding |
| Front Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Injection Molding |
| Nozzle Temperature | 190 – 220 °C | 374 – 428 °F | Injection Molding |
| Melt Temperature | 190 – 220 °C | 374 – 428 °F | Injection Molding |
| Mold Temperature | 40.0 – 70.0 °C | 104 – 158 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 – 4.00 hour | 2.00 – 4.00 hour | Injection Molding |
| Back Pressure | 29.4 – 58.8 MPa | 4260 – 8530 psi | Injection Molding |
| Screw Speed | 30 – 60 rpm | 30 – 60 rpm | Injection Molding |