LG Chemical ALPHALAC SH860 HIPS
| Manufacturer | LG Chemical |
| Trade Name | ALPHALAC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Injection Molding, General Purpose, Good ProcessabilityApplication: Refrigerator Inner LinerCAS No. 9003-55-8Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Melt Flow | 3.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
3.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238(G) |
| 10 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
10 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238(I) | |
| 43 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
43 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238(G) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | |
| Tensile Strength, Yield | 28.4 MPa
@Thickness 3.20 mm
|
4120 psi
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Break | 131 %
@Thickness 3.20 mm
|
131 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Yield | 5.0 %
@Thickness 3.20 mm
|
5.0 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Tensile Modulus | 2.16 GPa
@Thickness 3.20 mm
|
313 ksi
@Thickness 0.126 in
|
1mm/min; ASTM D638 |
| Flexural Yield Strength | 46.1 MPa
@Thickness 3.20 mm
|
6680 psi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Flexural Modulus | 1.67 GPa
@Thickness 3.20 mm
|
242 ksi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.588 J/cm
@Thickness 6.50 mm,
Temperature -30.0 °C |
1.10 ft-lb/in
@Thickness 0.256 in,
Temperature -22.0 °F |
ASTM D256 |
| 0.686 J/cm
@Thickness 3.20 mm,
Temperature -30.0 °C |
1.29 ft-lb/in
@Thickness 0.126 in,
Temperature -22.0 °F |
ASTM D256 | |
| 0.981 J/cm
@Thickness 6.50 mm,
Temperature 23.0 °C |
1.84 ft-lb/in
@Thickness 0.256 in,
Temperature 73.4 °F |
ASTM D256 | |
| 1.37 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
2.57 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C
@Thickness 6.40 mm
|
199 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 83.0 °C
@Thickness 6.40 mm
|
181 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Vicat Softening Point | 92.0 °C
@Load 5.00 kg
|
198 °F
@Load 11.0 lb
|
50°C/h; ASTM D1525 |
| Flammability, UL94 | HB
@Thickness >=1.60 mm
|
HB
@Thickness >=0.0630 in
|
|
| HB
@Thickness >=3.20 mm
|
HB
@Thickness >=0.126 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 170 – 190 °C | 338 – 374 °F | Injection Molding |
| Middle Barrel Temperature | 180 – 200 °C | 356 – 392 °F | Injection Molding |
| Front Barrel Temperature | 190 – 210 °C | 374 – 410 °F | Injection Molding |
| Nozzle Temperature | 190 – 220 °C | 374 – 428 °F | Injection Molding |
| Melt Temperature | 190 – 220 °C | 374 – 428 °F | Injection Molding |
| Mold Temperature | 40.0 – 70.0 °C | 104 – 158 °F | Injection Molding |
| Drying Temperature | 80.0 °C | 176 °F | Injection Molding |
| Dry Time | 2.00 – 4.00 hour | 2.00 – 4.00 hour | Injection Molding |
| Back Pressure | 29.4 – 58.8 MPa | 4260 – 8530 psi | Injection Molding |
| Screw Speed | 30 – 60 rpm | 30 – 60 rpm | Injection Molding |