LG Chemical HIPS 460AF PS, Flame Retardant
| Manufacturer | LG Chemical |
| Trade Name | HIPS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Injection Molding, PS, Flame RetardantApplication: Electric Parts Requiring Flame RetardancyCAS: 9003-55-8, 25713-60-4, 84852-53-9 and 1309-64-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0080 cm/cm
@Thickness 3.20 mm
|
0.0040 – 0.0080 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 14 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
14 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D785 |
| Tensile Strength, Yield | 23.0 MPa
@Thickness 3.20 mm
|
3340 psi
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Break | 60 %
@Thickness 3.20 mm
|
60 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Elongation at Yield | >= 5.0 %
@Thickness 3.20 mm
|
>= 5.0 %
@Thickness 0.126 in
|
50mm/min; ASTM D638 |
| Flexural Yield Strength | 37.3 MPa
@Thickness 3.20 mm
|
5400 psi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa
@Thickness 3.20 mm
|
313 ksi
@Thickness 0.126 in
|
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm
@Thickness 3.20 mm,
Temperature -30.0 °C |
0.735 ft-lb/in
@Thickness 0.126 in,
Temperature -22.0 °F |
ASTM D256 |
| 0.392 J/cm
@Thickness 6.40 mm,
Temperature -30.0 °C |
0.735 ft-lb/in
@Thickness 0.252 in,
Temperature -22.0 °F |
ASTM D256 | |
| 0.686 J/cm
@Thickness 6.40 mm,
Temperature 23.0 °C |
1.29 ft-lb/in
@Thickness 0.252 in,
Temperature 73.4 °F |
ASTM D256 | |
| 0.883 J/cm
@Thickness 3.20 mm,
Temperature 23.0 °C |
1.65 ft-lb/in
@Thickness 0.126 in,
Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C
@Thickness 6.40 mm
|
183 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C
@Thickness 6.40 mm
|
172 °F
@Thickness 0.252 in
|
Unannealed; ASTM D648 |
| Vicat Softening Point | 84.0 °C
@Load 5.00 kg
|
183 °F
@Load 11.0 lb
|
50°C/h; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C
@Thickness >=1.60 mm
|
122 °F
@Thickness >=0.0630 in
|
|
| 50.0 °C
@Thickness >=3.20 mm
|
122 °F
@Thickness >=0.126 in
|
||
| UL RTI, Mechanical with Impact | 50.0 °C
@Thickness >=1.60 mm
|
122 °F
@Thickness >=0.0630 in
|
|
| 50.0 °C
@Thickness >=3.20 mm
|
122 °F
@Thickness >=0.126 in
|
||
| UL RTI, Mechanical without Impact | 50.0 °C
@Thickness >=1.60 mm
|
122 °F
@Thickness >=0.0630 in
|
|
| 50.0 °C
@Thickness >=3.20 mm
|
122 °F
@Thickness >=0.126 in
|
||
| Flammability, UL94 | V-0
@Thickness >=1.60 mm
|
V-0
@Thickness >=0.0630 in
|
|
| V-0
@Thickness >=3.20 mm
|
V-0
@Thickness >=0.126 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 – 200 °C | 356 – 392 °F | Injection Molding |
| Middle Barrel Temperature | 190 – 200 °C | 374 – 392 °F | Injection Molding |
| Front Barrel Temperature | 200 – 210 °C | 392 – 410 °F | Injection Molding |
| Nozzle Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Melt Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | Injection Molding |
| Drying Temperature | 60.0 – 70.0 °C | 140 – 158 °F | Injection Molding |
| Dry Time | 3.00 – 4.00 hour | 3.00 – 4.00 hour | Injection Molding |
| Back Pressure | 29.4 – 58.8 MPa | 4260 – 8530 psi | Injection Molding |
| Screw Speed | 30 – 60 rpm | 30 – 60 rpm | Injection Molding |