LG Chemical KEYFLEX TO1192A Olefin Type TPE
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Injection Molding, TPV, General Purpose, Soft TouchApplication: Automotive InteriorCAS: 9003-07-0, 9010-79-1, 64742-54-7, 1333-86-4 and 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.930 g/cc | 0.930 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min
@Load 10.0 kg,
Temperature 230 °C |
20 g/10 min
@Load 22.0 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | <= 92 | <= 92 | ASTM D2240 |
| Elongation at Break | 700 %
@Thickness 2.00 mm
|
700 %
@Thickness 0.0787 in
|
50mm/min; ASTM D638 |
| Izod Impact, Notched | NB
@Thickness 6.40 mm,
Temperature 23.0 °C |
NB
@Thickness 0.252 in,
Temperature 73.4 °F |
ASTM D256 |
| NB
@Thickness 6.40 mm,
Temperature -40.0 °C |
NB
@Thickness 0.252 in,
Temperature -40.0 °F |
ASTM D256 | |
| Tear Strength | 53.9 kN/m | 308 pli | 50mm/min, @ Break; ASTM D624 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 – 200 °C | 356 – 392 °F | Injection Molding |
| Middle Barrel Temperature | 180 – 220 °C | 356 – 428 °F | Injection Molding |
| Front Barrel Temperature | 200 – 230 °C | 392 – 446 °F | Injection Molding |
| Nozzle Temperature | 200 – 240 °C | 392 – 464 °F | Injection Molding |
| Melt Temperature | 200 – 240 °C | 392 – 464 °F | Injection Molding |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | Injection Molding |
| Drying Temperature | 60.0 – 90.0 °C | 140 – 194 °F | Injection Molding |
| Dry Time | 3.00 – 4.00 hour | 3.00 – 4.00 hour | Injection Molding |
| Back Pressure | 29.4 – 58.8 MPa | 4260 – 8530 psi | Injection Molding |
| Screw Speed | 30 – 60 rpm | 30 – 60 rpm | Injection Molding |