LG Chemical LI-913 ASA, Injection Molding, High Impact
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ISO 1183 |
| Water Absorption | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 – 0.0060 cm/cm | 0.0030 – 0.0060 in/in | ISO 2577 |
| Melt Index of Compound | 6.955 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
6.955 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 25 % | 25 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.80 GPa | 261 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m²
@Temperature -30.0 °C
|
2.86 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180 |
| 42.0 kJ/m²
@Temperature 23.0 °C
|
20.0 ft-lb/in²
@Temperature 73.4 °F
|
ISO 80 | |
| Charpy Impact Unnotched | 7.00 J/cm²
@Temperature -30.0 °C
|
33.3 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179 |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 179 | |
| Charpy Impact, Notched | 0.600 J/cm²
@Temperature -30.0 °C
|
2.86 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179 |
| 4.50 J/cm²
@Temperature 23.0 °C
|
21.4 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 94.0 µm/m-°C
@Temperature 20.0 °C
|
52.2 µin/in-°F
@Temperature 68.0 °F
|
ISO 11359 |
| CTE, linear, Transverse to Flow | 116 µm/m-°C
@Temperature 20.0 °C
|
64.4 µin/in-°F
@Temperature 68.0 °F
|
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Annealed, 80°C, 4 hours; ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 94.0 °C | 201 °F | Annealed, 80°C, 4 hours; ISO 175 |
| Vicat Softening Point | 94.0 °C | 201 °F | 50 N, 50°C/h; ISO 306 |
| Flammability, UL94 | HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
|
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 250 °C | 428 – 482 °F | |
| Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Drying Temperature | 75.0 – 80.0 °C | 167 – 176 °F | |
| Dry Time | 2 – 4 hour | 2 – 4 hour | Predrying |